Evaluation of the compatibility induced by ionizing radiation on polymeric blends

To produce new polymers is a costly and time consuming task. Therefore, the utilization of existing polymers in form of blends enables to obtain new polymeric materials at a competitive cost. In this sense, polymer blending has become a growing scientific and commercial development activity. In most of the cases, polymeric blends have immiscible components and this represents an unbecoming situation on blend design. For such immiscible blends, it is required the use of compatibilizers to gain properties advantage. Compatibilization process can be achieved by chemical handling using additives and heat. On the other hand, ionizing radiation induces compatibilization by free radicals, which improve the dispersion and adhesion of the blend phases, without use of chemical additives and at room temperature. In this work, a polyamide 6.6/low-density polyethylene 75/25% wt/wt composition blend was electron beam irradiated up to 250 kGy, and thereafter mechanical tests were carried out. Tensile measurements have shown that the strength at break increases, the elongation at break decreases, the resistance to impact decreases and hardness increases when the radiation dose increases. Since this mechanical behavior is due to cross-linking and to the radiation induced blend compatibilization, this compatibility was evaluated by the approach of the glass transition temperatures for both components using DMA measurements. The results have shown that the glass transition temperatures of the blend components got closer in 8 deg C in the irradiated sample, when compared to the glass transition temperature values obtained for non-irradiated blend. (author)