Lithium alloying effect on critical temperature and glass-forming features in Bi-Sr-Ca-Cu-O system
- 1. Fiziko-tekhnicheskij Inst. im. A.F. Ioffe Rossijskoj Akademii Nauk, Sankt-Peterburg (Russian Federation)
Description
Glass-forming ability, structure and superconducting properties are investigated in Bi2.2Sr1.8Ca1.05Cu2.15LixOy, Bi2.2Sr1.8Ca1.05Cu2.15-xLixOy (x = 0, 0.3, 0.5, 0.7) compounds. The method of HF-melting at 1300-1500 deg C is used to produce the melts. Rapid quenching of melts results in a glassy state, the best glass-forming ability being observed with lithium in place of copper. The annealing of glass at 700-800 deg C gives the formation of a 2212 HTSC phase with critical temperature up to 91 K. In lithium doped specimens a superconducting phase forms at lower temperatures, shorter duration of annealing and is dependent on post-annealing cooling rate. The content and the properties of a 2212 phase vary nonmonotonically with annealing time. Lattice parameter c of a 2212 phase increase with lithium concentration
Abstract (Russian)
Исследованы стеклообразующая способность, структура и сверхпроводящие свойства соединений Bi2.2Sr1.8Ca1.05Cu2.15LixOy, Bi2.2Sr1.8Ca1.05Cu2.15-xLixOy (x = 0, 0.3, 0.5, 0.7). Расплавы соединений получались методом ВЧ-плавления при Т = 1300-1500 град С. Резкая закалка приводит к стеклообразным сплавам, у которых наилучшая стеклообразующая способность наблюдается при замещении меди на литий. Отжиг стекла при температурах 700-800 град С приводит к образованию высокотемпературной сверхпроводящей (ВТСП) фазы 2212 с критической температурой до 91 К. Для образцов, легированных литием, образование ВТСП-фазы происходит при меньших температурах, небольшой продолжительности отжига и зависит от скорости охлаждения после отжига. Параметр с кристаллической решетки фазы 2212 растет с увеличением содержания литияAdditional details
Additional titles
- Original title (Russian)
- Влияние легирования литием на критическую температуру и особенности стеклообразования системы Би-Ср-Cа-Cу-О
Publishing Information
- Journal Title
- Fizika Tverdogo Tela
- Journal Volume
- 41
- Journal Issue
- 1
- Journal Page Range
- p. 18-21
- ISSN
- 0367-3294
- CODEN
- FTVTAC
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 32004011
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- AMORPHOUS STATE; BISMUTH COMPOUNDS; CALCIUM COMPOUNDS; CHEMICAL COMPOSITION; CONCENTRATION RATIO; CUPRATES; ELECTRIC CONDUCTIVITY; HIGH-TC SUPERCONDUCTORS; LITHIUM COMPOUNDS; STRONTIUM COMPOUNDS; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0065-0273 K; TIME DEPENDENCE; TRANSITION TEMPERATURE; VITRIFICATION
- Descriptors DEC
- ALKALI METAL COMPOUNDS; ALKALINE EARTH METAL COMPOUNDS; COPPER COMPOUNDS; ELECTRICAL PROPERTIES; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; SUPERCONDUCTORS; TEMPERATURE RANGE; THERMODYNAMIC PROPERTIES; TRANSITION ELEMENT COMPOUNDS; TYPE-II SUPERCONDUCTORS
Optional Information
- Notes
- 15 refs., 3 figs.