Damage to the edge of steel stampings and abrasive during ultrasonic hydroabrasive machining

Principles have been established explaining the fracture of abrasive material in the process of ultrasonic hydroabrasive treatment, and a method is proposed suitable for the calculation of steel barb erosion in the hydroabrasive flux. It is assumed that fracture occurs along the entire edge surface and that the losses caused by plastic deformation are small. Conclusion has been made as to the governing the change of the abrasive particle size in the time of treatment. It is shown that the most serious fracture takes place at initial stage of the treatment, terminating practically after 60 minutes of operation. Curves showing the distribution of boron carbide abrasive particles are presented