Comparative study between sensitization degree of the 0.4% Mo austenitic stainless steel and UNS S31803 duplex stainless steel

This study aims at assessing the degree of susceptibility to intergranular corrosion of the UNS S31803 duplex stainless steel and the 0.4% Mo austenitic stainless steel through the double-loop electrochemical potentiodynamic reactivation (DL-EPR) test. Both steels were subjected to isothermal treatments at 650 deg C and 900 deg C in order to compare the effect of temperature on the respective degrees of sensitization. It was observed that the 0.4% Mo austenitic stainless steel presented a higher degree of sensitization and, consequently, a greater susceptibility to the intergranular corrosion process when compared to the UNS S31803 duplex stainless steel in the two temperatures studied. It was also observed that, for both steels, the heat treatment at 900 deg C resulted in a higher degree of sensitization when compared to the heat treatment at 650 deg C. (author)