Synthesis of nanocrystalline high-temperature zirconia phases

Creators

  • 1. Moskovskij Inzhenerno-Fizicheskij Inst. (Gosudarstvennyj Univ.), Moscow (Russian Federation)

Description

A study is made into the process of ZrO2 zirconium dioxide nanocrystal formation by heat treatment of amorphous zirconium hydroxide ZrO(OH)2. The possibility is shown for metastable high-temperature ZrO2 phases (tetragonal phase with traces of a cubic one) to be formed and preserved in powder nanoparticles with a CRA size of the order of 20 nm at 350-375 deg C. A temperature increase above 500-600 deg C results in the occurrence of a stable monoclinic phase and ib its content growth. The processes of thermal decomposition of hydroxides obtained from various zirconium salts are found to be different

Abstract (Russian)

Исследован процесс образования нанокристаллов диоксида циркония ZrO2 путем термообработки аморфного гидроксида циркония ZrO(OH)2. Показана возможность образования и сохранения метастабильных высокотемпературных фаз ZrO2 (тетрагональный со следами кубической) в наночастицах порошка с размером ОКР порядка 20 нм при 350-375 град С. Увеличение температуры выше 500-600 град С приводит к появлению и росту содержания стабильной моноклинной фазы. Обнаружено различие в процессах термического разложения гидроксидов, полученных из различных солей циркония

Additional details

Additional titles

Original title (Russian)
Синтез наноcристаллических высокотемпературных фаз диоксида циркония

Publishing Information

Journal Title
Neorganicheskie Materialy
Journal Volume
40
Journal Issue
3
Journal Page Range
p. 303-311
ISSN
0002-337X
CODEN
NEOMB8

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
36038101
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
AMORPHOUS STATE; CHEMICAL PREPARATION; CRYSTALLIZATION; CUBIC LATTICES; HEAT TREATMENTS; HYDROLYSIS; PARTICLE SIZE; PHASE STUDIES; POWDERS; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0400-1000 K; TEMPERATURE RANGE 1000-4000 K; TETRAGONAL LATTICES; ZIRCONIUM OXIDES
Descriptors DEC
CHALCOGENIDES; CHEMICAL REACTIONS; CRYSTAL LATTICES; CRYSTAL STRUCTURE; DECOMPOSITION; LYSIS; OXIDES; OXYGEN COMPOUNDS; PHASE TRANSFORMATIONS; SIZE; SOLVOLYSIS; SYNTHESIS; TEMPERATURE RANGE; TRANSITION ELEMENT COMPOUNDS; ZIRCONIUM COMPOUNDS

Optional Information

Notes
16 refs., 13 figs.