Effect of elemental composition of ion beam on the phase formation and surface strengthening of structural materials

Creators

  • 1. Lipetskij Gosudarstvennyj Tekhnicheskij Univ., Lipetsk (Russian Federation)

Description

The investigation results are reported on the influence of ion beam element composition on phase formation, wear resistance and microhardness of surface layers of titanium alloys VT-4 and VT-16 as well as stainless steel 12Kh18N10T implanted with nitrogen, oxygen and boron. It is stated that ion implantation into structural materials results in surface hardening and is directly dependent on element composition of implanted ion beam. The presence of oxygen in boron or nitrogen ion beams prevents the formation of boride and nitride phases thus decreasing a hardening effect

Abstract (Russian)

Представлены результаты исследования влияния элементного состава пучка ионов при имплантации азота, кислорода и бора на фазообразование, износостойкость и микротвердость поверхностных слоев титановых сплавов ВТ-4 и ВТ-16, а также нержавеющей стали 12Х18Н10Т. Установлено, что имплантация ионов в конструкционные материалы приводит к упрочнению поверхности этих материалов и находится в непосредственной зависимости от элементного состава пучка имплантируемых ионов. Присутствие кислорода в пучке ионов бора или в пучке ионов азота препятствует образованию боридных и нитридных фаз, снижая эффект упрочнения

Additional details

Additional titles

Original title (Russian)
Влияние элементного состава пучка ионов на фазообразование и упрочнение поверхности конструкционных материалов

Publishing Information

Journal Title
Fizika Metallov i Metallovedenie
Journal Volume
92
Journal Issue
6
Journal Page Range
p. 103-107
ISSN
0015-3230
CODEN
FMMEA9

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
34014495
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
ALLOY-TI90MO7AL2; BORON ISOTOPES; FORMATION HEAT; ION BEAMS; ION IMPLANTATION; KEV RANGE 01-10; KEV RANGE 10-100; MELTING POINTS; MICROHARDNESS; NITROGEN IONS; OXYGEN IONS; PHASE STUDIES; STEEL-CR18NI10TI; SURFACE HARDENING; WEAR
Descriptors DEC
ALLOYS; ALUMINIUM ALLOYS; AUSTENITIC STEELS; BEAMS; CARBON ADDITIONS; CHARGED PARTICLES; CHROMIUM ALLOYS; CHROMIUM-NICKEL STEELS; CORROSION RESISTANT ALLOYS; ENERGY RANGE; ENTHALPY; HARDENING; HARDNESS; HEAT RESISTANT MATERIALS; HEAT RESISTING ALLOYS; HIGH ALLOY STEELS; IONS; IRON ALLOYS; IRON BASE ALLOYS; ISOTOPES; KEV RANGE; MATERIALS; MECHANICAL PROPERTIES; MOLYBDENUM ALLOYS; NICKEL ALLOYS; PHYSICAL PROPERTIES; REACTION HEAT; STAINLESS STEELS; STEELS; SURFACE TREATMENTS; THERMODYNAMIC PROPERTIES; TITANIUM ADDITIONS; TITANIUM ALLOYS; TITANIUM BASE ALLOYS; TRANSITION ELEMENT ALLOYS; TRANSITION TEMPERATURE

Optional Information

Notes
3 refs., 5 figs., 3 tabs.