Electrical resistance of La0.63Ca0.37MnO3 films biaxially mechanically stressed by a substrate in the process of their growth

Creators

  • 1. RAN, Fiziko-Tekhnicheskij Inst. im. A.F. Ioffe, Sankt-Peterburg (Russian Federation)

Description

The analysis of the electroresistance of the (20 nm) La0.63Ca0.33MnO3 films, grown coherently on the monocrystalline substrates with significant negative and close to zero displacement in the crystalline lattice parameters, is carried out. The elementary cell volume in the manganite film depended on the substrate lattice parameters. At T < 200 K and μ0H = 0 the electroresistance of the La0.63Ca0.33MnO3 films, grown on the (001) LaAlO3, by several orders of the value exceeded the corresponding data on the manganite films, formed on the (001) La0.29Sr0.71Al0.65Ta0.35O3. The conductivity degradation of the elastically stressed manganite films (biaxial compression) constitutes the consequence of the superstoichiometric (≅ 45%) relative concentration of the Mn+4 ions in their volume

Abstract (Russian)

Проведен анализ электросопротивления пленок (20 нм) La0.63Ca0.33MnO3 , выращенных когерентно на монокристаллических подложках со значительным отрицательным и близким к нулю рассогласованием в параметрах кристаллических решеток. Объем элементарной ячейки в манганитной пленке зависел от параметра решетки подложки. При T < 200 K и μ0H = 0 электросопротивление пленок La0.63Ca0.33MnO3, сформированных на (001) LaAlO3, на несколько порядков величины превышало соответствующие данные для манганитных пленок, выращенных на (001) La0.29Sr0.71Al0.65Ta0.35O3. Деградация проводимости упругонапряженных (двухосное сжатие) манганитных пленок является следствием сверхстехиометрической (≅ 45%) относительной концентрации ионов Mn+4 в их объеме

Additional details

Additional titles

Original title (Russian)
Электросопротивление пленок Ла

Publishing Information

Journal Title
Pis'ma v Zhurnal Tekhnicheskoj Fiziki
Journal Volume
30
Journal Issue
13
Journal Page Range
p. 12-18
ISSN
0320-0116
CODEN
PZTFDD

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
37011275
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
CALCIUM OXIDES; EPITAXY; LANTHANUM OXIDES; LATTICE PARAMETERS; MAGNETORESISTANCE; MANGANESE OXIDES; STRESSES; SUBSTRATES; THIN FILMS; VAPOR DEPOSITED COATINGS
Descriptors DEC
ALKALINE EARTH METAL COMPOUNDS; CALCIUM COMPOUNDS; CHALCOGENIDES; COATINGS; CRYSTAL GROWTH METHODS; ELECTRIC CONDUCTIVITY; ELECTRICAL PROPERTIES; FILMS; LANTHANUM COMPOUNDS; MANGANESE COMPOUNDS; OXIDES; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; RARE EARTH COMPOUNDS; TRANSITION ELEMENT COMPOUNDS

Optional Information

Notes
12 refs., 2 figs.