Synthesis of Copper nanoparticles through vesicle template using gamma irradiation

Nano technology has gained attention for its application in life. This study was conducted to produce copper (Cu) nanoparticles using gamma ray irradiation through template vesicles. Cu nanoparticle has a variety of applications such as capacitor materials, catalyst, conductive coating, high thermal conductivity materials as well as lubricant additives. this study used gamma radiation compared to other methods because the use of gamma rays in producing nanoparticle is safer and environmental friendly. The purpose of this study was to see the effects of radiation on the formation of Cu nanoparticles. The radiation dose used was 80 kGy and 100 kGy. The vesicles were formed by mixing water, sodium n-lauroyl sarcosinat hydrated, 1-decanol and polyethylene glycol with certain ratio (85 %: 5 %: 7 %: 3 %). Analysis from the transmission electron microscopy (TEM) showed the production of multilammelar vesicles in size between 30 nm-80 nm. The formation of nanoparticles was analyzed using UV-Vis absorption spectroscopy, X-ray diffraction (XRD) and transmission electron microscopy (TEM). Analysis of UV-Vis absorption spectroscopy showed no resonance peak around 600 nm. XRD analysis confirmed the presence of Cu, Cu2O and CuO. Analysis and characterisation using transmission electron microscopy (TEM) also confirmed that nanoparticles were produced with different sizes according to the radiation dose. At the radiation dose of 80 kGy, nanoparticles size is found vary between 30 nm to 90 nm. While at the radiation dose of 100 kGy, nanoparticles size is found vary between 3 nm to 7 nm. From this study it can be concluded that higher radiation dse will produce smaller nanoparticles. (author)