Irradiation effects of the zirconium oxidation and the uranium diffusion in zirconia

The context of this study is the direct storage of spent fuel assemblies after operation in reactor. In order to obtain data on the capacities of the can as the uranium diffusion barrier, a fundamental study has been carried out for modelling the internal cladding surface under and without irradiation. The behaviour of zirconium in reactor conditions has at first been studied. A thin uranium target enriched with fissile isotope has been put on a zirconium sample, the set being irradiated by a thermal neutrons flux leading to the fission of the deposited uranium. The energetic history of the formed fission products has revealed two steps: 1)the zirconium oxidation and 2)the diffusion of uranium in the zirconia formed at 480 degrees C. A diffusion coefficient under irradiation has been measured. Its value is 10-15 cm2.s-1. In order to be able to reveal clearly the effect of the irradiation by the fission products on the zirconium oxidation, measurements of thermal oxidation and under 129Xe irradiation have been carried out. They have shown that the oxidation is strongly accelerated by the irradiation and that the temperature is negligible until 480 degrees C. On the other hand, the thermal diffusion of the uranium in zirconium and in zirconia has been studied by coupling ion implantation and Rutherford backscattering spectroscopy. This study shows that the uranium diffuses in zirconium and is trapped in zirconia in a UO3 shape. (O.M.)