SiO2-TiO2-P2O5 meso porous coatings for proton exchange membranes fuel cells

The article describes the preparation of meso porous SiO2-TiO2-P2O5 coatings by Sol-Gel process combined to EISA method for using as proton exchange membranes fuel cells. Tetraethyl orthosilicate (TEOS), methyl triethoxysilane (MTES), titanium tetrachloride (TiCl4) and phosphorus trichloride (PCl3) have used as precursors and cetyl trimethylammonium bromide (CTAB) as porous generator agent. Films were deposited by immersion technique controlling the relative humidity at 40 and 20-70% and treated at 400 to 500 degree centigrade for 15, 30, 45 and 60 min. The variation of the refractive index and thickness have studied as a function of temperature and sintering time as well as the pore volume and density of the coatings by spectroscopic ellipsometry. Moreover, the hydrophobic/hydrophilic character of the coatings has been studied by Transform Infrared Spectroscopy (FTIR) and by contact angle measurements, following the loss of methyl groups with the temperature and sintering time. The results show that these parameters are crucial to obtain coatings with high porosity and low contact angle, important to obtain high proton conductivity conditions. The sintering conditions were fixed to 400 degree centigrade/60 min. Conductivity measurements at four points show high proton conductivity, 0,16 and 0,85 S/cm, up and down ramp, respectively, at 80 degree centigrade and 80 % of humidity. These coatings are good candidates for PEMFC membranes, if they are deposited onto electrodes. (Author)