¹³C NMR and XPS characterization of anion adsorbent with quaternary ammonium groups prepared from rice straw, corn stalk and sugarcane bagasse

Highlights: • ¹³C NMR and XPS were successfully used to characterize quaternary ammonium groups in the surface of crop straw based anion adsorbents. • The results obtained from different kinds of crop straw material clearly confirmed the presence of quaternary ammonium groups. • The composition of C-groups and N-groups also were determined by curving fitting of high-resolution XPS C1 and N1 spectra. - Abstract: Despite amino groups modified crop straw has been intensively studied as new and low-cost adsorbent for removal of anionic species from water, there is still a lack of clear characterization for amino groups, especially quaternary ammonium groups in the surface of crop straw. In this study, we used ¹³C NMR and XPS technologies to characterize adsorbents with quaternary ammonium groups prepared from rice straw, corn stalk and sugarcane bagasse. ¹³C NMR spectra clearly showed the presence of quaternary ammonium groups in lignocelluloses structure of modified crop straw. The increase of nitrogen observed in XPS survey spectra also indicated the existence of quaternary ammonium group in the surface of the adsorbents. The curve fitting of high-resolution XPS N1s and C1s spectra were conducted to probe the composition of nitrogen and carbon contained groups, respectively. The results showed the proportion of quaternary ammonium group significantly increased in the prepared adsorbent's surface that was dominated by methyl/methylene, hydroxyl, quaternary ammonium, ether and carbonyl groups. This study proved that ¹³C NMR and XPS could be successfully utilized for characterization of quaternary ammonium modified crop straw adsorbents.