Irradiation embrittlement of pressure vessel steels
Creators
- 1. Skoda, Plzen (Czechoslovakia)
- 2. Ustav Jaderneho Vyzkumu, Rez (Czechoslovakia)
Description
A Standard Research Programme on Irradiation Embrittlement of Pressure Vessel Steels was approved by the Coordinating Meeting on the 12th May 1972 at the Working Group on Engineering Aspects of Irradiation Embrittlement of Pressure Vessel Steels. This Working Group was set up by the International Atomic Energy Agency in Vienna. Seven countries with their research institutes agreed on doing irradiation experiments according to the approved programme on steel A533 B from the U.S. HSST Programme. The Czechoslovak contribution covering tensile and impact testing of non-irradiated steel and steel irradiated at 280degC to 1.3 x 1023 n/m2 (E above 1 MeV) is presented in this report. As an additional part the same set of experiments was carried out on two additional steels - A 542 and A 543, made in SKODA Works for comparison of their irradiation embrittlement and hardening with A533 B steel. (author)
Files
7229078.pdf
Files
(12.2 MB)
| Name | Size | Download all |
|---|---|---|
|
md5:c06983126c35084ae624340d935c6b3c
|
12.2 MB | Preview Download |
Additional details
Additional titles
- Subtitle (English)
- Test report
Publishing Information
- Imprint Title
- Co-ordinated research programme on irradiation embrittlement of pressure vessel steels
- Imprint Pagination
- p. 243-261.
- Report number
- IAEA--176
Conference
- Title
- Research co-ordination meeting on irradiation embrittlement of reactor pressure vessel steels.
- Dates
- 23 Oct 1974.
- Place
- Vienna, Austria.
INIS
- Country of Publication
- International Atomic Energy Agency (IAEA)
- Country of Input or Organization
- International Atomic Energy Agency (IAEA)
- INIS RN
- 7229078
- Subject category
- S42: ENGINEERING;
- Resource subtype / Literary indicator
- Conference
- Descriptors DEI
- CHARPY TEST; COMPARATIVE EVALUATIONS; COORDINATED RESEARCH PROGRAMS; DUCTILE-BRITTLE TRANSITIONS; ELONGATION; EMBRITTLEMENT; IRRADIATION; PRESSURE VESSELS; RADIATION HARDENING; STEEL-ASTM-A533-B; STEEL-ASTM-A542; STEEL-ASTM-A543; TENSILE PROPERTIES; YIELD STRENGTH
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; CARBON STEELS; CONTAINERS; DESTRUCTIVE TESTING; HARDENING; IMPACT TESTS; IRON ALLOYS; IRON BASE ALLOYS; MATERIALS TESTING; MECHANICAL PROPERTIES; MECHANICAL TESTS; PHYSICAL RADIATION EFFECTS; RADIATION EFFECTS; RESEARCH PROGRAMS; STEELS; TESTING; TRANSITION ELEMENT ALLOYS