Multiple Ion Exchange Column Tests for Technetium Removal from Hanford Tank Waste Supernate

Five cycles of loading, elution, and regeneration were performed to remove technetium from a Hanford waste sample retrieved from Tank 241-AW-101 using SuperLig 639 resin. The waste sample was diluted to 4.95 M Na plus and then was processed to remove 137Cs through dual ion exchange columns each containing 15 mL of SuperLig 644. To remove 99Tc, the cesium decontaminated solution was processed downwards through two ion exchange columns, each containing 12 mL of SuperLig 639 resin. The columns, designated as lead and lag, each had an inside diameter of 1.45 cm and a height of 30 cm. The columns were loaded in series, but were eluted and then regenerated separately. The average technetium loading for the cycles was 250 BV at 10 percent breakthrough. There was no significant difference in the loading performances among the five cycles. The percent removal of 99Tc was greater than 99.94 percent and the average decontamination factor (DF) was approximately 1.7 x 103. Approximately 99 percent of the 99Tc loaded on the resin was eluted with less than 15 BV of de-ionized water at 65 degrees C