Phase diagram of the Mn2V2O7-Mg2V2O7 system below the solidus
- 1. Inst. Khimii Tverdogo Tela UrO RAN, Ekaterinburg (Russian Federation)
- 2. AOZT Chelyabinskij Nauchno-Vnedrencheskij Tsentr METALLURGIYA (Russian Federation)
- 3. AMOZT V-kompleks, Ozersk, Chelyabinskoj Obl. (Russian Federation)
Description
Phase equilibria between manganese and magnesium pyrovanadates in subsolidus region were studied by the method of high-temperature X-ray phase analysis. It has been ascertained that solid solutions on the basis of all modifications of both compounds are the pyrovanadates interaction equilibrium products. It is shown that a reversible polymorphous transformation at 20±5 deg C occurs in Mn2V2O7. With increase in magnesium concentration in Mn2(1-x)Mg2xV2O7, where 0≤x≤0.25, the phase transition temperature increases up to 190±10 deg C. Formation of substitution solid solution on the basis of magnesium pyrovanadate Mg2(1-y)Mn2yV2O7, where 0≤y≤0.02, decreases thermal stability of α-modification from 760±5 deg C to the room temperature, further substitution for up to 70 mol.% Mn2V2O7 stabilizes solid solution of the structure β-Mg2V2O7 at room temperature. Thermal stability of solid solutions Mg2(1-y)Mn2yV2O7, where 0≤y≤0.70, with the structure β-Mg2V2O7 decreases from 915±5 to 620±5 deg C with growth of manganese ions concentration
Abstract (Russian)
Методом температурного рентгенофазового анализа изучены фазовые равновесия между пированадатами марганца и магния в субсолидусной области. Установлено, что равновесными продуктами взаимодействия пированадатов являются твердые растворы на основе всех модификаций обоих соединений. Показано, что в Mn2V2O7 происходит обратимое полиморфное превращение при 20±5 град. С. С увеличением концентрации магния в Mn2(1-x)Mg2xV2O7, где 0≤x≤0,25, температура фазового перехода повышается до 190±10 град. С. Образование твердого раствора замещения на оснвое пированадата магния Mg2(1-y)Mn2yV2O7, где 0≤y≤0,02, понижает термическую устойчивость α-модификации от температуры 760±5 град. С до комнатной, дальнейшее замещение до 70 мол.% Mn2V2O7 стабилизирует при комнатной температурое твердый раствор со структурой β-Mg2V2O7. Термическая устойчивость твердых растворов Mg2(1-y)Mn2yV2O7, где 0≤y≤0,70, со структурой β-Mg2V2O7 понижается от 915±5 до 620±5 град. С с ростом концентрации ионов марганцаAdditional details
Additional titles
- Original title (Russian)
- Диаграмма состояния системы Мн
Publishing Information
- Journal Title
- Zhurnal Neorganicheskoj Khimii
- Journal Volume
- 44
- Journal Issue
- 3
- Journal Page Range
- p. 485-488
- ISSN
- 0044-457X
- CODEN
- ZNOKAQ
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 31035393
- Subject category
- S37: INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY;
- Descriptors DEI
- CHEMICAL COMPOSITION; CONCENTRATION RATIO; CRYSTAL-PHASE TRANSFORMATIONS; EQUILIBRIUM; LATTICE PARAMETERS; MAGNESIUM COMPOUNDS; MANGANESE COMPOUNDS; PHASE DIAGRAMS; PHASE STUDIES; SENSITIVITY; SOLID SOLUTIONS; TEMPERATURE RANGE 0273-0400 K; TEMPERATURE RANGE 0400-1000 K; TRANSITION TEMPERATURE; VANADATES; X-RAY DIFFRACTION
- Descriptors DEC
- ALKALINE EARTH METAL COMPOUNDS; COHERENT SCATTERING; DIAGRAMS; DIFFRACTION; DISPERSIONS; INFORMATION; MIXTURES; OXYGEN COMPOUNDS; PHASE TRANSFORMATIONS; PHYSICAL PROPERTIES; SCATTERING; SOLUTIONS; TEMPERATURE RANGE; THERMODYNAMIC PROPERTIES; TRANSITION ELEMENT COMPOUNDS; VANADIUM COMPOUNDS
Optional Information
- Notes
- 10 refs., 2 figs.