Phase transformations in the Y2Cu2O5-BaCuO2 system
Creators
- 1. Inst. Fiziki Tverdogo Tela i Poluprovodnikov NAN Belorussii, Minsk (Belarus)
- 2. Inst. Obshchej i Neorganicheskoj Khimii im. N.S. Kurnakova RAN, Moscow (Russian Federation)
Description
The sequence of the phase transformations in the Y2Cu2O5-BaCuO2 pseudobinary system by heating and cooling within the temperature range of 1170-1310 K is studied. It is established that the reaction zone of the BaCuO2/Y2Cu2O5 diffusion pair consists of the BaCuO2/YBa2Cu3O7-δ/Y2BaCuO5/Y2O3/Y2Cu2O5, which points at the sequence of the phase transformations by the YBa2Cu3O7-δ phase crystallization within the temperature range of 1170-1220 K. It is established, that at 1260-1310 K there takes place the formation and growth of the BaCu2O2 compound. It is shown, that the YBa2Cu3O7-δ crystallization occurs by the Y2Cu2O5 + 4.3BaCuO2 mixture cooling within the wide temperature range of 1240-1190 K and depends on the availability the BaCu2O2 compound in the solution-melt on the Y2BaCuO5 grains boundaries and free access of the gaseous phase oxygen
Abstract (Russian)
Исследована последовательность фазовых превращений в псевдобинарной системе Y2Cu2O5-BaCuO2 при нагревании и охлаждении в интервале 1170-1310 К. Показано, что реакционная зона диффузионной пары BaCuO2/Y2Cu2O5 состоит из слоев BaCuO2/YBa2Cu3O7-δ/Y2BaCuO5/Y2O3/Y2Cu2O5, что указывает на последовательность фазовых превращений при кристаллизации фазы YBa2Cu3O7-δ в диапазоне 1170-1220 К. Обнаружено, что при 1260-1310 К происходит образование и рост соединения BaCu2O2. Показано, что кристаллизация YBa2Cu3O7-δ при охлаждении смеси Y2Cu2O5 + 4.3BaCuO2 происходит в широком температурном диапазоне 1240-1190 К и зависит от наличия в растворе-расплаве соединения BaCu2O2 на границах зерен Y2BaCuO5 и свободного доступа кислорода газовой фазыAdditional details
Additional titles
- Original title (Russian)
- Фазовые превращения в системе Ы
Publishing Information
- Journal Title
- Neorganicheskie Materialy
- Journal Volume
- 38
- Journal Issue
- 5
- Journal Page Range
- p. 602-606
- ISSN
- 0002-337X
- CODEN
- NEOMB8
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 34047003
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- BARIUM OXIDES; CERAMICS; COPPER OXIDES; CRYSTALLIZATION; GRAIN BOUNDARIES; MICROSTRUCTURE; PHASE STUDIES; PHASE TRANSFORMATIONS; SUPERCONDUCTIVITY; TEMPERATURE RANGE 1000-4000 K; YTTRIUM OXIDES
- Descriptors DEC
- ALKALINE EARTH METAL COMPOUNDS; BARIUM COMPOUNDS; CHALCOGENIDES; COPPER COMPOUNDS; ELECTRIC CONDUCTIVITY; ELECTRICAL PROPERTIES; MICROSTRUCTURE; OXIDES; OXYGEN COMPOUNDS; PHASE TRANSFORMATIONS; PHYSICAL PROPERTIES; TEMPERATURE RANGE; TRANSITION ELEMENT COMPOUNDS; YTTRIUM COMPOUNDS
Optional Information
- Notes
- 7 refs.; 1 tab.; 4 figs.