Improvement in technology for smelting the high alloy chromium-containing steel

Creators

  • 1. Moskovskij Gosudarstvennyj Inst. Stali i Splavov, (Russian Federation)

Description

Theoretical analysis of deep decarbonization of chromium-bearing melts on stainless steel melting is accomplished. It is shown that deep decarbonization conditions can be provided on high-chromium steel (05Kh18N10T and 08Kh17T) melting when using the following flow sheet: an arc furnace - a ladle-furnace unit - a vacuum chamber for oxygen-argon decarbonization. Such processing procedure makes it possible to obtain the melts with low carbon contents (0.02-0.06)% and high chromium contents (15-20)% without application of low-carbon ferrochrome, an arc furnace being used for charge material melting only

Abstract (Russian)

Проведен теоретический анализ глубокого обезуглероживания хромсодержащих расплавов при выплавке нержавеющей стали. Показано, что условия глубокого обезуглероживания могут быть обеспечены при выплавке высокохромистых сталей (08Х18Н10Т и 08Х17Т) при использовании технологической схемы: дуговая печь - установка ковш-печь - вакуумная камера кислород-аргонного обезуглероживания. Такая технология позволяет получать расплавы с низким содержанием углерода (0,02-0,06)% и высоким содержанием хрома (15-20)% без применения низкоуглеродистого феррохрома, при этом дуговая печь используется только для плавления шихты

Additional details

Additional titles

Original title (Russian)
Совершенствование технологии выплавки высоколегированной хромсодержащей стали

Publishing Information

Journal Title
Izvestiya Vysshikh Uchebnykh Zavedenij. Chernaya Metallurgiya
Journal Issue
no.3
Journal Page Range
p. 23-26
CODEN
IVUMAX

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
36060575
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
ARC FURNACES; ARGON; CHEMICAL COMPOSITION; CHEMICAL REACTIONS; CONCENTRATION RATIO; FLOWSHEETS; MELTING; OPTIMIZATION; OXYGEN; STEEL-CR18NI10TI; THERMODYNAMIC PROPERTIES
Descriptors DEC
ALLOYS; AUSTENITIC STEELS; CARBON ADDITIONS; CHROMIUM ALLOYS; CHROMIUM-NICKEL STEELS; CORROSION RESISTANT ALLOYS; DIAGRAMS; ELECTRIC FURNACES; ELEMENTS; FLUIDS; FURNACES; GASES; HEAT RESISTANT MATERIALS; HEAT RESISTING ALLOYS; HIGH ALLOY STEELS; INFORMATION; IRON ALLOYS; IRON BASE ALLOYS; MATERIALS; NICKEL ALLOYS; NONMETALS; PHASE TRANSFORMATIONS; PHYSICAL PROPERTIES; RARE GASES; STAINLESS STEELS; STEELS; TITANIUM ADDITIONS; TITANIUM ALLOYS; TRANSITION ELEMENT ALLOYS

Optional Information

Notes
3 refs., 1 fig.