Radiation synthesis of polymer polyol

The polymer polyol was synthesized by γ irradiation. The properties of polymer polyol synthesized with different radiation dose were studied. The experiment result showed the radiation dose hadn't significant influence on the hydroxyl value of polymer polyol. The sample with different solid content had different hydroxyl value. When the radiation dose is between 1 to 12 kGy, the viscosity and hydroxyl value of polymer polyol were increased with the increment of radiation dose. When radiation dose is between 1 to 12 kGy, with the increment of radiation dose, viscosity of polymer polyol was rapidly increased, and the content solid of sample has few change. When radiation dose is higher than 20 kGy, the viscosity and hydroxyl value of polymer polyol have gradually increase with the increment of radiation dose. The size of polymer particles is 0.1-0.6 μm. The value of 150 mesh filter was 100%. The polymer polyol may be used as PU foam and elastomer. (authors)