Mechanical properties of irradiated and non-irradiated Zr1%Nb and Zircaloy claddings

The mechanical properties of irradiated and non-irradiated Zr1%Nb were determined and they were compared with the analogous properties of Zircaloy-4 to establish connections between the evolution of mechanical parameters of Zr1%Nb and Zircaloy-4 cladding materials and the measure of irradiation. Samples were irradiated in the vertical channels of the Budapest Research Reactor for different time periods at 50-65 C temperature. The measure of irradiation (fluent) for different samples was estimated by means of flux measurement and using the effective irradiation time. Post irradiation uniaxial tension tests in transverse direction were carried out on ring specimens. The mechanical parameters of the Zr1%Nb alloy significantly improve due to the effect of irradiation. However, the values of mechanical parameters do not further increase when the fluent increases above 1020 n/cm2. These results are in good accordance with the Russian ones [1]. Contrary to the behaviour of Zr1%Nb alloy, the mechanical parameters of the Zircaloy practically do not change on the effect of irradiation. The originally high values of ultimate tensile strength and yield stress change only slightly with the increasing fluent in the investigated fluent-region. (Author)