Deuterium absorption property of Al/Zr-V/Mo multifilms

Deuterium absorption property of Al/Zr-V/Mo multifilms was studied experimentally to explore the effect of Al film. There is only one desorption peak at 320 degree C for Al film, two desorption peaks at 220 degree C and 350 degree C for Zr-V film. When the average thickness of Al film is less than 0.6 μm, the desorption property of Al/Zr-V multifilms is just as Zr-V film, when it is more than 0.6 μm, just as Al film. Deuterium absorption by Al/Zr-V multifilms decreases as the thickness of Al film increases until 0.7 μm, then the deuterium absorption no longer changes significantly. The Al film of multifilms cracks on desorbing, so the absorption rate varies as Zr-V film when the thickness of Al film is less than 0.6 μ. When the thickness of Al film is more than 0.6 μm, the deuterium absorption rate of multifilm does not change with the thickness of Al film. (author)