Photocatalytic decomposition of 2-chlorophenol in aqueous solution by UV/TiO2 process with applied external bias voltage

The decomposition of 2-chlorophenol by UV/TiO2 process with the application of external bias voltage was examined in this study. Experiments were conducted in a batch reactor using TiO2-coated titanium sheet as anode and platinum sheet as cathode. The anode photocatalysis of 2-chlorophenol was totally inhibited for experiments conducted with the application of external anodic bias voltage lower than the flat band potential of TiO2. The decomposition rate of 2-chlorophenol was then increased with increasing external anodic bias voltage applied up to 0.0 V (versus SCE). The application of external bias voltage higher than 1.0 V did not markedly promote the photocatalysis of 2-chlorophenol possibly because the photocurrent induced was constant. Experimental results indicated that the decomposition of 2-chlorophenol was more effective for experiments conducted in acidic solutions due to the lower flat band potential of TiO2 and the higher photocurrent induced. The presence of electron scavengers in aqueous solution, such as oxygen molecules, may increase the decomposition rate of 2-chlorophenol. However, the effect of dissolved oxygen was diminished for experiments conducted with applied external bias voltage. The photocatalytic decomposition rate of 2-chlorophenol was enhanced linearly with the increasing UV light intensity when the external bias voltage was applied