VUV-induced degradation of FEP Teflon aboard LDEF

Examination of fluorinated ethylene propylene (FEP) copolymer materials recovered from the Long Duration Exposure Facility (LDEF) reveals differing damage characteristics on leading edge (ram-facing) versus trailing edge (wake-facing surfaces). Silver/Teflon (Ag/FEP) thermal control materials on ram facing surfaces of the LDEF exhibited obvious degradation, with an apparent increase in diffuse light scattering, whereas identical materials on the wake facing surfaces showed little apparent damage with cursory inspection. Microscopic examination of both types of surfaces reveals the nature and extent of environment induced degradation of materials. The ram facing surfaces were clearly eroded by atomic oxygen impingement, while the wake facing material developed a thin, highly embrittled surface layer