InSb thin films grown by electrodeposition

We have grown InSb thin films on Cu substrates using the electrodeposition technique. The electrochemical bath from which the InSb thin films were grown was made up of a mixture of aqueous solutions of 0.05 M InCl3 and 0.03M SbCl3, 0 .20M citric acid and 0.30M sodium citrate. Citric acid and sodium citrate were used as complexing agents to bring the reduction potential of In and Sb closer to maintain binary growth. The electrodeposited films were characterized by structural, morphological and optical studies. X-ray diffraction studies show that the films are polycrystalline InSb having the zinc blende structure. Scanning electron microscopy (SEM) studies reveal that the surface of the films is uniformly covered with submicron sized spherical particles. FTIR spectra of InSb thin films show a sharp absorption peak at wave number 1022 cm−1 corresponding to the band gap. Hot probe analysis shows that the InSb thin films have p type conductivity