Fabrication of barium/strontium carbonate coated amorphous carbon nanotubes as an improved field emitter

Amorphous carbon nanotubes (aCNTs) were synthesized by a chemical reaction between ferrocene and ammonium chloride at a temperature ∝250 circle C in an air furnace. As-synthesized aCNTs were coated with the barium/strontium carbonate through a simple chemical process. The coating of barium/strontium carbonate was confirmed by a high resolution transmission electron microscopy, X-ray diffraction, and Fourier transformed infrared spectroscopy. Morphology of the as-prepared samples was studied by field emission scanning electron microscopy. Thermal gravimetric analysis showed that barium/strontium carbonate coated aCNTs are more stable than the pristine aCNTs. As-prepared barium/strontium carbonate coated aCNTs showed significantly improved field emission properties with a turn-on field as low as 2.5 V/μm. The variation of field emission characteristics of the barium/strontium carbonate coated aCNTs with interelectrode distances was also studied. (orig.)