Ductile to brittle transition of U--0.75 wt% Ti penetrator cores
Description
V-notch Charpy impact specimens were machined from U--0.75 wt percent Ti penetrator cores supplied by the Air Force Armament Laboratory. The response of these specimens to impact loads at various temperatures was measured. The data indicated that the impact energy required to cause fracture was a function of temperature and appeared to be insensitive to microstructural and hardness variations. All tests from --54 to 3000C indicated a brittle condition with data fitting the impact energy = 4.41e0.0048/sup t/ equation
Availability note (English)
MF available from INIS under the Report Number; Available from NTIS.
Files
Restricted
The record is publicly accessible, but files are restricted to users with access.
Additional details
Publishing Information
- Imprint Pagination
- 10 p.
- Report number
- LA--6064-MS
INIS
- Country of Publication
- United States
- Country of Input or Organization
- United States
- INIS RN
- 7257294
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CHARPY TEST; DUCTILE-BRITTLE TRANSITIONS; FRACTURES; HARDNESS; HIGH TEMPERATURE; LOW TEMPERATURE; MEDIUM TEMPERATURE; MICROSTRUCTURE; STRESSES; TEMPERATURE DEPENDENCE; TITANIUM ADDITIONS; URANIUM BASE ALLOYS; VARIATIONS
- Descriptors DEC
- ACTINIDE ALLOYS; ALLOYS; CRYSTAL STRUCTURE; DESTRUCTIVE TESTING; FAILURES; IMPACT TESTS; MATERIALS TESTING; MECHANICAL PROPERTIES; MECHANICAL TESTS; TESTING; URANIUM ALLOYS
Optional Information
- Notes
- Available from NTIS. $4.00.