Preparation and characterization of Chitosan/Konjac glucomannan/CdS nanocomposite film with low infrared emissivity

Novel organic-inorganic nanocomposite films were prepared with Chitosan (CS), Konjac glucomannan (KGM) and CdS by one-step synthesis. As-prepared films were characterized by IR spectra, transmission electron microscopy (TEM), scanning electron microscopy (SEM) and infrared emissometer (IR). The results indicated that grown CdS dendrites were formed with reaction time of 12 h for Cd2+ and CS/KGM, and were well dispersed in CS/KGM with an average diameter of 40 nm. The CS/KGM/CdS nanocomposite films had significantly low infrared emissivity. When the mole ratio of CdS to summation of CS and KGM construction units was 1.0 with CdS size of 10-20 nm, the film got the lowest infrared emissivity value of 0.011, which could be attributed to the strong synergism effect existing between CS/KGM and CdS dendrites.