Sintering of Si C by hot-pressing with addition of Al2O3 and concentrate of rare earths

Silicon carbide (SiC) has essentially covalent bonds (∼88%). The high covalency bond is responsible for the good mechanical properties, although it induces a low self diffusion coefficient, making densification more difficult. For a successful densification is necessary to apply pressure on the samples, and/or the addition of sintering additives, which improves the densification. In this SiC samples with alumina (Al2O3) and concentrate of rare earth (CRE) addition were sintered by hot pressing in argon atmospheric at 20 MPa of pressure, heating rate of 20 deg C/min up to 1800 deg C and a dwell time of 1 h. Initially the CRE was calcined at 1000 deg C during 1 h. After that, three mixtures were prepared with distinct concentrations in high energy mill and the samples were sintered. The aim of this work is to improve SiC densification by the liquid phase formation during sintering owing to the additives reactions between itself. The pressure intensify the driving force for densification, taking the liquid phase to drain easier through the grain boundaries, making possible best accommodation and rearrangement of the grains. The application of the pressure on the samples during sintering contributes to improve densification and becomes possible sintering in lower temperature than conventional one. The phases of the sintered samples were analyzed by X-ray diffraction and the morphology were verified by scanning electron microscopy. (author)