Synthesis and characterization of orthorhombic TlSr2CuO5
Creators
- 1. E.I. Dupont de Nemours and Co., Wilmington, DE (United States)
Description
TlSr2CuO5 has been synthesized in polycrystalline form. Powder X-ray diffraction studies indicate an orthorhombic structure; space group Pmmm; α = 3.661(2), b = 3.793(1), c = 8.999(3) angstrom. The presence of short Cu-O bonds indicates the high formal valence for Cu. TlSr2CuO5 is found to be metallic and no superconductivity could be observed down to 4.2K
Additional details
Publishing Information
- Journal Title
- Journal of Solid State Chemistry
- Journal Volume
- 93
- Journal Issue
- 1
- Journal Page Range
- p. 250-255.
- ISSN
- 0022-4596
- CODEN
- JSSCBI
INIS
- Country of Publication
- United States
- Country of Input or Organization
- United States
- INIS RN
- 24014251
- Subject category
- S36: MATERIALS SCIENCE; S36: MATERIALS SCIENCE;
- Descriptors DEI
- CHEMICAL PREPARATION; COPPER OXIDES; CRYSTAL STRUCTURE; ELECTRIC CONDUCTIVITY; OPTIMIZATION; ORTHORHOMBIC LATTICES; POWDERS; STRONTIUM OXIDES; SUPERCONDUCTIVITY; SYNTHESIS; TEMPERATURE RANGE 1000-4000 K; THALLIUM COMPOUNDS; THALLIUM OXIDES; X-RAY DIFFRACTION
- Descriptors DEC
- ALKALINE EARTH METAL COMPOUNDS; CHALCOGENIDES; COHERENT SCATTERING; COPPER COMPOUNDS; CRYSTAL LATTICES; DIFFRACTION; ELECTRICAL PROPERTIES; OXIDES; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; SCATTERING; STRONTIUM COMPOUNDS; TEMPERATURE RANGE; TRANSITION ELEMENT COMPOUNDS