Crack propagation and acoustic emission behavior of silver-added Dy123 bulk superconductor

The relationship between the crack propagation process and acoustic emission (AE) signals was investigated in 3-point bending tests in which stress loading was applied parallel to the c-axis of U-notched specimens cut from Dy123 bulk superconductors with and without the addition of silver (Ag). The average bending stress of the specimens containing 10 mass% of Ag was approximately 20% higher than that of the specimens without the addition of Ag; the total AE energy of the former specimens was approximately fourfold greater than that of the latter specimens. However, cracks initiated in all of the specimens at a bending stress level of around 25 MPa, regardless of the presence or absence of Ag. An analysis of the amplitude distribution revealed that the failure mode was matrix failure in both types of specimens. Cracks in the low-strength specimens without Ag propagated between gas holes or along cleavage planes, and the AE event count and total AE energy were low. By contrast, the high-strength Ag-added specimens had fewer gas holes and cleavage cracks on account of their improved microstructure. In these samples, crack propagation orthogonal to the cleavage planes caused Ag particles to separate from the matrix and induced cleavage cracks. The addition of Ag presumably had the effect of inhibiting crack propagation, with the result that the AE event count and AE energy increased. The results of this study indicate that failure phenomena can be interpreted by evaluating the amplitude distribution, AE event count and total AE energy. This suggests that the AE method is also applicable to evaluations of bulk superconductors