Mechanical and magnetic relaxation measurements on doped and undoped nickel after electron irradiation and stretching
Description
Mechanical and magnetic relaxation measurements have been performed on doped and undoped nickel single crystals after electron irradiation and a tensile stress treatment. The mechancial damping measurement showed that in the prober deformed by mechanical stress, interstitial atoms exist after tempering at about 1000C which are preferably oriented in the <100>-direction. The results of relaxation measurement are independent with respect to Cu and Fe doping rates up to 100 ppm; this indicates the existence of deformation-induced lattice imperfections, the dumbbell-type interstitial atom. The orientation dependence described previously is in accord with our evaluations. The damping maximum of the first isochrone is strongly affected by defect-induced atomic motions and the tempering process. (GSC)
Availability note (English)
Available from the library of the Stuttgart Univ.Abstract (German)
An dotierten und undotierten Nickel-Einkristallen wurden nach Elektronenbestrahlung und Zugverformung mechanische und magnetische Relaxationsmessungen vorgenommen. In den mechanischen Daempfungsmessungen zugverformter Proben konnte nach Anlassen auf etwa 1000C ein orientierungsfaehiges Zwischengitteratom mit <100>-Vorzugsachsel nachgewiesen werden. Die Unabhaengigkeit der Relaxationsmessungen von Cu- bzw. Fe-Dotierungen bis etwa 100 ppm weist auf eine verformungsinduzierte Eigenfehlstelle, das Hantel-Zwischengitteratom, hin. Die frueher beschriebene Orientierungsabhaengigkeit stimmt mit den eigenen Auswertungen ueberein. Das Daempfungsmaximum der 1. Isochrone ist stark von den versetzungsinduzierten Atombewegungen und vom Ausheilen gepraegt. (GSC)Additional details
Additional titles
- Original title (German)
- Mechanische und magnetische Relaxationsmessungen an dotiertem und undotiertem Nickel nach Elektronenbestrahlung und Zugverformung
Publishing Information
- Imprint Pagination
- 60 p.
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 8333479
- Subject category
- S75: CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY;
- Resource subtype / Literary indicator
- Thesis, Non-conventional Literature
- Descriptors DEI
- ACTIVATION ENERGY; ANNEALING; COPPER ADDITIONS; DAMPING; ELECTRON BEAMS; INTERSTITIALS; IRON ADDITIONS; MONOCRYSTALS; NICKEL; PHYSICAL RADIATION EFFECTS; RELAXATION; STRAINS
- Descriptors DEC
- BEAMS; CRYSTAL DEFECTS; CRYSTAL STRUCTURE; CRYSTALS; ELEMENTS; ENERGY; HEAT TREATMENTS; LEPTON BEAMS; METALS; PARTICLE BEAMS; POINT DEFECTS; RADIATION EFFECTS; TRANSITION ELEMENTS
Optional Information
- Notes
- 23 figs.; 10 refs.; with tabs.