Effect of Sc/Zr ratio on the microstructure and mechanical properties of new type of Al–Zn–Mg–Sc–Zr alloys

The rare earth scandium (Sc) as a microalloying element has attracted an increasing interest in aluminum alloys for achieving excellent mechanical properties. Combining with zirconium, high strength and low price Al–Sc alloys are expected. The effects of Sc and Zr on the grain refinement, recrystallization resistance and precipitation hardening were investigated in new type of Al–Zn–Mg–Sc–Zr alloys by rolling, annealing and aging processes. Scandium addition into the Al–Zn–Mg alloys can efficiently refine the grain size and increase recrystallization resistance, especially together with zirconium addition. The maximum value of the yield-to-tensile strength (627 MPa/667 MPa) was obtained with 0.2Sc/0.4Zr ratio of the alloy after solution-aging treatment. The additional strengthening of the alloys is attributed to the grain refinement and the precipitation-strengthening effect of Al₃Sc, Al₃Zr or Al₃(Sc, Zr) in the proper ratio of Sc/Zr during aging