Phase transformations in titanium-copper system alloys
Creators
- 1. Inst. Fiziki Metallov UrO RAN, Ekaterinburg (Russian Federation)
Description
Structure of titanium-copper system alloys containing 5-13 at.% copper upon heat treatment with various rates and tempering was studied. Conditions for the metastable β-phase formation within that system were determined. β-phase was shown to be kept in the metastable state in that system alloys starting from 9 at.% of copper and higher upon heat treatment with 103 deg/s rate. Tempering of Ti-13 at.% Cu alloy under 400 deg C during 30 min. resulted in occurrence of diffusion scattering on electron diffraction pattern and in occurrence of a banded contrast on a photograph of the structure that vanished upon tempering of the alloy under 450 deg C - 15 min. Upon heat treatment with ∼ 2.75 x 102 deg/s rate in all the investigated alloys one observed the eutectoid decomposition. The interface of MH martensite transformation within that system under room temperature fell within 9 - 11 at.% of copper
Abstract (Russian)
Изучена структура сплавов системы титан-медь с содержанием меди от 5 до 13 ат.% после закалки с различными скоростями и отпуска. Определены условия образования в этой системе метастабильной β-фазы. Показано, что β-фаза сохраняется в метастабильном состоянии в сплавах этой системы, начиная с 9 ат.% меди и больше, после закалки со скоростью 103 град/с. Отпуск сплава Ti-13 ат.% Cu при 400 град С - 30 мин приводит к появлению на электронограммах дифузного рассеяния и полосчатого контраста на снимках структуры, исчезающего после отпуска этого же сплава при 450 град. С - 15 мин. После закалки со скоростью примерно 2,75 х 102 град/с во всех исследованных сплавах протекает эвтектоидный распад. Граница мартенситного превращения МH в этой системе при комнатной температуре проходит между 9 и 11 ат.% медиAdditional details
Additional titles
- Original title (Russian)
- Фазовые превращения в сплавах системы титан-медь
Publishing Information
- Journal Title
- Fizika Metallov i Metallovedenie
- Journal Volume
- 89
- Journal Issue
- 5
- Journal Page Range
- p. 47-53
- ISSN
- 0015-3230
- CODEN
- FMMEA9
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 32016201
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- BINARY ALLOY SYSTEMS; CONCENTRATION RATIO; COPPER ALLOYS; CRYSTAL-PHASE TRANSFORMATIONS; HARDNESS; HEAT TREATMENTS; LATTICE PARAMETERS; MICROSTRUCTURE; PHASE STUDIES; TITANIUM BASE ALLOYS
- Descriptors DEC
- ALLOY SYSTEMS; ALLOYS; MECHANICAL PROPERTIES; PHASE TRANSFORMATIONS; TITANIUM ALLOYS; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- 6 refs., 6 figs.