The effect of heat treatment and alloying with hydrogen on the structure and deformability of titanium alloys at room temperature

Creators

  • 1. AO OKB Sukhogo, Moscow (Russian Federation)
  • 2. MATI-RGTU, Moscow (Russian Federation)

Description

Methods of X-ray diffraction and metallographic analysis as well as cold pressing tests are applied to study the influence of hydrogen absorption and heat treatments of hot worked rods of titanium alloys VT5, VT6, VT16, VT22I, VT35, TS6 and Ti-10-2-3 on their cold ductility. The use of hydrogen technology to enhance cold ductility is stated to be promising for titanium alloys with a coefficient of β-phase stabilization approximately equal to 1. For every alloy the hardening temperature and the cooling rate are determined which provide the optimum phase composition for performing cold working

Abstract (Russian)

Методами рентгеноструктурного и металлографического анализов, а также механическими испытаниями на сжатие проведено исследование влияния наводороживания и термической обработки горячедеформированных прутков титановых сплавов ВТ5, ВТ6, ВТ16, ВТ22И, ВТ35, ТС6 и Ti-10-2-3 на их технологическую пластичность при деформировании в холодном состоянии. Установлено, что применение водородной технологии для улучшения деформируемости в холодном состоянии является перспективным для титановых сплавов с коэффициентом стабилизации β-фазы, приблизительно равным 1. Для каждого сплава определены температуры нагрева под закалку и скорости охлаждения, обеспечивающие оптимальный фазовый состав для осуществления обработки давлением вхолодную

Additional details

Additional titles

Original title (Russian)
Влияние термической обработки и легирования водородом на структуру и деформируемост' титановых сплавов при нормальной температуре

Publishing Information

Journal Title
Metallovedenie i Termicheskaya Obrabotka Metallov
Journal Issue
no.5
Journal Page Range
p. 17-21
ISSN
0026-0819
CODEN
MTOMAX

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
34067449
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
ABSORPTION; ALLOY-TI88MO8AL3; ALLOY-TI90AL6V4; ALLOY-TI90MO7AL2; COLD WORKING; DUCTILITY; HYDROGEN; PHASE STUDIES; QUENCHING; RODS; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0400-1000 K
Descriptors DEC
ALLOYS; ALUMINIUM ALLOYS; CHROMIUM ALLOYS; ELEMENTS; FABRICATION; IRON ADDITIONS; IRON ALLOYS; MATERIALS WORKING; MECHANICAL PROPERTIES; MOLYBDENUM ALLOYS; NONMETALS; SORPTION; TEMPERATURE RANGE; TENSILE PROPERTIES; TITANIUM ALLOYS; TITANIUM BASE ALLOYS; TRANSITION ELEMENT ALLOYS; VANADIUM ALLOYS

Optional Information

Notes
7 refs.; 4 figs.