Modification of 40X13 steel at high-intensity nitrogen ion implantation

This paper presents the results of the formation of deep modified layers in 40X13 steel using a high-intensity repetitively pulsed nitrogen ion beam with a current density up to 0.25 A/cm². An arc generator with a hot cathode provided the DC nitrogen plasma flow. A plasma immersion approach was used for high-frequency, short-pulse very intense nitrogen ion beam formation. A grid hemisphere with radii of 7.5 cm was immersed in the plasma. Negative bias pulses with an amplitude of 1.2 kV, a pulse duration of 4 μs, and a pulse repetition rate of 10⁵ pulses per second were applied to the grid. The substrates were implanted at the temperature of 500 °C and various processing times ranging from 20 to 120 minutes with 1.2 keV nitrogen ions using a very-high current density up to 0.25 A/cm² ion beams. The work explores the surface morphology, elemental composition, and mechanical properties of deep-layer modified 40X13 steel after low ion energy, very-high-intensity nitrogen ion beam implantation. (paper)