Extraction of cellulose nanofibers from Pinus oocarpa residues

Full text: Pinus oocarpa, which wood is moderately hard and tough, is planted in Brazil for reforestation and employed for timber production used in constructions. The wood residues, such as shavings, bark and sawdust represent 30% to 50% of the total volume of wood production, of which the sawdust is 10%¹. Cellulose nanofibers is nanomaterials having a diameter between 5 nm and 20 nm and a length of up to hundreds of nm. To obtain nanofibers from cellulose sources, such as sisal and sugarcane bagasse, is used chemical processes, in which the lignocellulosic material initially undergoes pre-treatments to promote partial separation of the cellulose, such as mercerisation and bleaching thus disposing lignin and hemicellulose components. Sequentially, by controlled acid hydrolysis, amorphous regions of the cellulose are removed, and crystalline cellulose is isolated in the form of cellulose nanofibers. In this work, nanofibers from sawdust of Pinnus oocarpa, containing 44.8 wt% of cellulose 20.6 wt% hemicellulose and 30.0 wt% insoluble lignin were isolated by mercerisation (NaOH 5%, 80°C, 120 min), followed by bleaching (NaOH + acetic acid + NaClO₂, 80 deg C, 240min) and acid hydrolysis (60 wt% sulfuric acid, 45 °C, 40min). Nanofibers obtained were characterized by DRX and SEM-FEG. Results showed that, for used conditions, fiber acid hydrolysis was not complete, therefore a biphasic suspension was formed. Crystallinity index achieved was not much higher than that from pinus fiber itself, increasing from 62% to 65% and signs of cellulose type II were observed. SEM images showed elongated fibers, which have diameter of 15 ± 5 nm and length of hundreds of nm, what means that they have a large L/D aspect ratio. Nanofiber extraction yield was very low (1.3 wt% of initial residue). All steps of the process are being reviewed aiming at better results. 1) Morais, S. A. L.; Nascimento E. A. e D. C. Melo, 2005, R. Árvore, 29, 3, 461-470. (author)