The magneto-elastic anisotropy due to dislocations in (100) oriented magnetic films

The magneto-elastic anisotropy due to edge and screw dislocations on commonly observed slip planes in Ni(100), Fe(100), and Ni-Fe(100) single crystal films has been calculated using a single domain treatment. The magnetization is assumed to be constrained to the film plane by magneto-static forces. The results show that both dislocation types give dominantly uniaxial anisotropies in all three materials. The magnitude of the anisotropy varies inversely with distance from the core and in a complex fashion around the core. Also the easy direction varies around the core. The data are presented for the three materials and the qualitative agreement with magnetization ripple observations is shown to be good. Es wird die durch Stufen- und Schraubenversetzungen hervorgerufene magnetoelastische Anisotropie von normalerweise beobachteten Gleitebenen in Ni(100)-, Fe(100)- und Ni- Fe(100)-Einkristallschichten mit einer Ein-Domänenbehandlung berechnet. Dabei wird angenommen, daß die Magnetisierung durch magnetostatische Kräfte auf die Schichtebene beschränkt ist. Die Ergebnisse zeigen, daß beide Versetzungsarten in allen drei Materialien vorherrschend uniaxiale Anisotropien ergeben. Die Größe der Anisotropie ändert sich invers mit dem Abstand vom Kern und in einer komplexen Weise um den Kern herum. Auch die leichte Richtung variiert um den Kern herum. Die Werte für die drei Materialien werden angegeben und eswird gezeigt, daß die qualitative Übereinstimmung mit Ripple-Beobachtungen der Magnetisierung gut ist.