Physical-mechanical properties and structure of coating in hard alloy on the base of Cr2C3-Ni

Creators

  • 1. Sumskij Inst. Modifikatsii Poverkhnosti, Sumy (Ukraine)
  • 2. Belorusskij Gosudarstvennyj Univ., Minsk (Belarus)
  • 3. Natsional'nyj Univ., Kafedra Yadernoj Fiziki, Tashkent (Uzbekistan)

Description

The coatings based on a chromium carbide - nickel mixture were deposited on a copper substrate with use of highspeed plasma jet. The formation of solid solution on the base of Ni, chromium carbide Cr7C3, intermetallide Cr3Ni2, and CrO were revealed by XRD. The characteristic relief due to dynamical interaction of melting and flash powder particles was observed on surface. Hardness of coating was 66±4.5 HRC and the coating adhesion as for substrate was changed from 25 up to 300 MPa in dependence on treatment regime

Abstract (Russian)

С помощью высокоскоростной плазменной струи были нанесены покрытия из смеси карбида хрома с никелем на подложку из технической меди. Проведенный рентгеновский микроанализ покрытия выявил образование твердого раствора на основе Ni, а также карбида хрома Cr7С3, интерметаллида Cr3Ni2 и, возможно, оксида CrO. На поверхности наблюдали характерный рельеф, связанный с динамическим взаимодействием расплавленных и оплавленных частиц порошка. Твердость покрытия на отдельных участках поверхности составляет 66±4.5 HRC, а адгезия покрытия к подложке колеблется от 25 до 300 МПа в зависимости от режима обработки

Additional details

Additional titles

Original title (Russian)
Физико-механические свойства и структура покрытия из твердого сплава на основе Cр

Publishing Information

Journal Title
Poverkhnost'. Rentgenovskie, Sinkhrotronnye i Nejtronnye Issledovaniya
Journal Issue
no.7
Journal Page Range
p. 48-52
ISSN
1028-0960

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
38029779
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
ADHESION; CHROMIUM CARBIDES; COPPER; HARDNESS; MIXTURES; MORPHOLOGY; NICKEL ALLOYS; PHASE STUDIES; PLASMA ARC SPRAYING; SPRAYED COATINGS; SUBSTRATES; TURBINE BLADES; USES
Descriptors DEC
ALLOYS; CARBIDES; CARBON COMPOUNDS; CHROMIUM COMPOUNDS; COATINGS; DEPOSITION; DISPERSIONS; ELEMENTS; MECHANICAL PROPERTIES; METALS; SPRAY COATING; SURFACE COATING; TRANSITION ELEMENT ALLOYS; TRANSITION ELEMENT COMPOUNDS; TRANSITION ELEMENTS