[en] An investigation of the resistance to void swelling of the ferritic steel FV448 has been made in electron irradiation experiments in a High Voltage Electron Microscope. Overaged samples of vacuum-remelted FV448 showed zero swelling after irradiation to doses of up to 30 dpa, in the temperature range 400 to 550⁰C. The resistance to void swelling was due to the absence of mutual interaction between interstitial loops. Impurity segregation to the loops, and precipitation, prevented continuous dislocation climb, thus removing biased sinks from the system at low doses. An interstitial-impurity binding energy of 0.5 eV was measured, suggesting that the impurity responsible was carbon or nitrogen. Some effects attributable to the heating of thin foils in the HVEM environment were detected. (author)