[en] A year long study has been made of the effect of fatigue on the bond between two epoxy encapsulant formulations and a fused alumina disc. The variables studied included isothermal aging at temperatures up to and including the cure temperature and cyclic thermal aging from +74 to -54⁰C. The encapsulants were glass microballoon filled epoxies differing only in curing agents. One was cured with an aromatic amine eutectic (Shell Curing Agent Z). The other was cured with diethanolamine. The Z cured encapsulant bond failed completely at the bond interface with little or no aging; infrared evidence indicated a soluble interlayer as a possible cause of failure. The diethanolamine cured encapsulant survived a year of isothermal aging with little or no evidence of bond degradation. Cyclic thermal aging resulted in gradual bond failure with time. An extrapolation of the cyclic aging data indicates that the stresses induced by thermal cycling would result in complete bond failure in about 1200 days