[en] We have analyzed the tensile behavior of 11 heats of grades CF8-CPF8-304H and 13 heats of grades CF8M-CPF8M-316H static and centrifugal castings from room temperature to 650⁰C. Except for anomalous conditions, the centrifugal castings exhibited uniform composition. All CPF8-304H centrifugal castings contained only radial columnar grains, but some CPF8M-316H castings had columnar, banded, or equiaxed structures. Ultimate tensile strength and total elongation were the properties in which castings showed the most inferiority to wrought material. With increasing ferrite content, 0.2% yield strength and ultimate tensile strength increased while uniform elongation, total elongation, and reduction of area decreased. Although centrifugal castings did not exhibit significant end-to-end variation in tensile behavior, the 0.2% yield strength displayed anisotropy, with axial and circumferential values being greater than radial