[en] This paper discusses the degradation mechanisms affecting the residual life of the nuclear pressurized water reactor (PWR) pressurizer and its subcomponents. The major sources of degradation for pressurizers are thermal transients such as plant heatups and cooldowns, internal pressure within the vessel, high intermittent flow through the spray nozzle, differential thermal movement causing rubbing of the immersion heater sheathes, and prolonged exposure to chemical and thermal conditions that can potentially lead to degradation. The latter includes thermal embrittlement of cast stainless steel spray heads and chemically assisted intergranular stress corrosion cracking of stainless steel. Steam leakage that interacts with lubricants used to assemble manway bolted joints can cause corrosion of bolts