AbstractAbstract
[en] In the present work ferritic weld metals of hyperbaric MIG/MAG welds with pressures up to 100 bar were examined. As a result of the pressure, interactions with the shielding gas, the filler metal as well as with the welding parameters had to be expected and were consequently included in the analysis. Investigation was focused on the influence of these parameters on the chemical composition of the weld metals, the microstructure and toughness behaviour, including fracture mechanics test. Using quantitative microstructural analysis as well as fractography a correlation between microstructure and toughness has been shown. (orig.)
[de]
In der vorliegenden Arbeit wurden ferritische Schweissgueter aus hyperbaren MIG/MAG-Schweissverbindungen bei Druecken bis zu 100 bar untersucht. Da durch den Druck auch Wechselwirkungen mit dem Schutzgas, dem Schweisszusatzwerkstoff sowie den Schweissparametern zu erwarten sind, wurden auch diese Einfluesse punktuell in die Untersuchungen mit einbezogen. Dabei konzentrieren sich die Untersuchungen auf den Einfluss dieser Groessen auf die chemische Zusammensetzung des Schweissgutes, die Mikrostruktur und die Zaehigkeit inklusive bruchmechanischer Tests. Mit Hilfe quantitativer Gefuegeanalysen sowie fraktographischer Untersuchungen liess sich eine Korrelation zwischen der Mikrostruktur und der Zaehigkeit aufzeigen. (orig.)Original Title
Gefuege und Zaehigkeit von ferritischem Schweissgut aus hyperbaren Schweissverbindungen
Primary Subject
Secondary Subject
Source
1988; 120 p; Diss.
Record Type
Report
Literature Type
Thesis/Dissertation
Report Number
Country of publication
Reference NumberReference Number
INIS VolumeINIS Volume
INIS IssueINIS Issue