[en] The precipitation strengthening of modified chronium steels is effected predominantly by M23C6 carbides. In molybdenum-modified 9% chromium steels, creep resistance depends on the dispersion of the M23C6 carbides and on the molybdenum content in the solid solution. There is no point in increasing molybdenum contents of molybdenum-modified steels above approximately 1 wt.%. In vanadium-modified steels precipitation strengthening is effected both by M23C6 carbides and by VCxNy carbonitrides. If the amount of nitrogen in solid solution is insufficient, this reduces the volume fraction of VCxNy in the structure and thus impairs the creep resistance of the steel. It is advisable to restrict the aluminium and titanium contents in the vanadium-modified. (orig.)
[de]
An der Ausscheidungshaertung von modifizierten Chromstaehlen ist vor allem das Carbid M23C6 beteiligt. In Mo-modifizierten 9%-Chromstaehlen haengt die Zeitstandfestigkeit von der Dispersion des Carbids M23C6 und vom Mo-Gehalt in fester Loesung ab. Es gibt keinen Grund, den Mo-Gehalt in diesen Staehlen ueber die 1%-Grenze hinaus zu erhoehen. In V-modifizierten Staehlen beteiligen sich an der Ausscheidungshaertung neben M23C6-Carbiden auch die Carbonitride VCxNy. Wenn in der festen Loesung keine ausreichende Stickstoffmenge vorhanden ist, verringert sich im Gefuege der VCxNy-Volumenanteil, und dadurch verschlechtert sich die Warmfestigkeit des Stahls. In V-modifizierten Chromstaehlen sollte deshalb der Al- und Ti-Gehalt, der den effektiven N-Gehalt in fester Loesung verringert, beschraenkt werden. (orig.)Journal