[en] In the pressurised heavy water reactor systems of India, the fuel is encapsulated in thin-walled tubes (0.342 mm) closed with endcaps by resistance welding. The integrity of these fuel elements should be such that no fission gas leakage takes place during reactor operation. The quality control of the endcap welds needed to satisfy this requirement includes helium leak test and destructive metallographic test (on sample basis). This paper discusses the feasibility study that has been carried out in the author's laboratory to develop an immersion ultrasonic test method for evaluating the integrity of the endcap weld region. Through holes of various sizes (0.15mm, 0.2mm, 0.4mm diameter and 0.185mm and 0.342mm deep) were machined by spark erosion machining at the weld joints to simulate defects of various sizes. Line focussed probe of 10 MHz frequency was used for the testing. It was possible to detect clearly all the machined holes. Based on the above standardised procedure, further testing was done on endcap welds which were rejected during fabrication on account of showing leak rate of 3 x 10^-6 std. c.c/sec. or more during helium leak test. Though it was possible to get echoes from the natural defects in the rejected tubes with echo amplitude of 70%, the signal was accompanied by the geometrical reflection (noise) giving an amplitude of 20% from the weld region, giving rise to the problem of resolving the defect indication from the geometric indications. Therefore, signal analysis approach was adopted. The signal obtained from the weld zone were subjected to various analysis procedures like a) autopower spectrum, b) total energy content and c) demodulated auto correlation function. It was possible by all the three methods to differentiate the defect signal from those due to weld geometry or due to noise. Subsequently, metallography was carried out to characterise the type of defects observed during the ultrasonic testing. (author). 4 figs