[en] In order to clarify the high-temperature deformation behaviour and the origin of threshold stress of ODS martensite steel with Y₂O₃ particles, the stress-strain curves were measured by compression test at 600 to 700degC and at strain rates from 2x10^-5 to 2x10^-3s^-1, and the threshold stress was measured by stress abruptly loading test (SAL test) at 650degC. Further, the possibility of temperature dependence of threshold stress was discussed by estimating the activation energy for dislocations to detach the Y₂O₃ particles. The results are summarized as follows. 1) The stress exponents of ODS martensite steel were 22-35. And the activation energy of high-temperature deformation was 742 kJ/mol. Those deformation behaviour of ODS martensite steel agrees with the deformation behaviour of ODS ferritic steel. 2) The Orowan stress and the void-hardening stress calculated from dispersion parameters approximately agreed with the threshold stress obtained by SAL test. It is concluded that the originating mechanism of the threshold stress in ODS martensite steel is the Srolovitz's one. 3) The calculated activation energy for a dislocation to detach the particles was very high compared to the thermal energy. Therefor, the threshold stress is almost independent of temperature. (author)