[en] The regularities of defect substructure formation in alloy V-0.45% Zr-0.2% C (at. %) are studied in the process of stress relaxation using transmission electron microscopy. Mechanical stresses in the alloy are generated by a pulsed proton and carbon ion beam with power density of 5 x 107 W/cm2. The substructural studies are performed at various distances from the specimen surface. Through the whole depth of an ion-modified layer the intense development of collective (rotation) relaxation modes of mentioned stresses is revealed. Main structural types of forming plastic flow localization zones are established. Specific features of defect fine structure of these zones are investigated and their possible dislocation-disclination models are considered. The nature of activation of collective rotation modes of mechanical stress relaxation is under discussion
[ru]
Методом просвечивающей электронной микроскопии в сплаве V-0.45% Zr-0.2% C (ат. %) изучены закономерности формирования дефектной структуры в процессе релаксации механических напряжений, генерируемых импульсным пучком протонов и ионов углерода с плотностью мощности 5 х 107 Вт/см2 на разном расстоянии от облучаемой поверхности. Обнаружено интенсивное развитие коллективных (ротационных) мод релаксации указанных напряжений по всей глубине ионно-модифицированного слоя. Выявлены основные структурные типы формирующихся при этом зон локализации пластического течения, изучены особенности тонкой дефектной микроструктуры этих зон и рассмотрены их возможные дислокационно-дисклинационные модели. Обсуждается природа активизации коллективных ротационных мод релаксации механических напряжений, генерируемых мощным ионным пучкомJournal