[en] Effect of the structure of antidiffusion barrier TaC layer between tungsten and graphite layers on carbon diffusion rate through the barrier layer into tungsten at rapid heating up to high temperature has been studied. At heating up to 3225 deg C with the rate of 215 deg C/s and 40 s holding time, a ternary W-Ta-C eutectic is formed on the W-TaC interface which crystallizes as a complicated ternary compound WxTayCz. It is shown the carbon diffusion rate is slow in two-phase tantalum carbide with subcarbide phase ζ-Ta4C3 compared to that in single-phase structure. The composition and microhardness of eutectic zone on tungsten-tantalum-carbide interface in these structures are different too
[ru]
Изучено влияние структуры карбида тантала, применяемого в качестве противодиффузионного барьерного слоя между вольфрамом и графитом, на скорость диффузии атомов углерода через барьерный слой в вольфрам при быстром высокотемпературном нагреве. При нагреве до температуры 3225 град С со скоростью 215 град С/с и последующей изотермической выдержке в течение 40 с на границе W-TaC образуется тройная эвтектика W-Ta-C, которая кристаллизуется в виде сложного тройного соединения WxTayCz. Показано, что диффузия углерода в двухфазный карбид тантала, содержащий в своем составе субкарбидную фазу ζ-Ta4C3, протекает менее интенсивно, чем в однофазных структурах. При этом меняются состав и микротвердость эвтектических зон на границе вольфрам-карбид танталаJournal