[en] One measured the sputtering coefficients for various carbon materials in 90 eV ion average energy oxygen plasma flow. The tendency for sputtering coefficient increase from 0.67 up to 0.96 at reduction of the crystalline structure perfection level in the line of materials is observed. Presence of 15% of boron in carbon-devitrified glass results in decrease of the sputtering coefficient up to 0.25 in contrast to 0.96 of a structurally close pyrocarbon. This value by one order exceeds the values obtained at sputtering by deuterium ions implying the essential contribution of sputtering by oxygen impurity ions into the emission of impurities in thermonuclear reactors
[ru]
Измерены коэффициенты распыления различных материалов в потоке кислородной плазмы со средней энергией ионов 90 эВ. Наблюдается тенденция роста коэффициента рапыления от 0,67 до 0,96 при снижении степени совершенства кристаллической структуры в ряду материалов. Наличие 15% бора в составе углесилата приводит к уменьшению коэффициента распыления до 0,25 по сравнению с 0,96 у близкого по структуре пироуглерода. Это значение на порядок превышает значения, полученные при распылении ионами дейтерия, что указывает на существенный вклад распыления примесными ионами кислорода в эмиссию примесей в термоядерных реакторахJournal
Izvestiya Akademii Nauk. Rossijskaya Akademiya Nauk. Seriya Fizicheskaya; ISSN 1026-3489; 
; CODEN IRAFEO; v. 64(4); p. 747-751
; CODEN IRAFEO; v. 64(4); p. 747-751