[en] Crystal structure of Mn2(PxV1-x)(VyP1-y)O7 solid solution: a 6.794(2), b = 8.621(4), c = 4.271(2)A, β = 104.07(3) deg, sp.gr. Cm, Z 2, ρ(calc.) = 3.74 g/cm3, was determined by the method of X-ray diffraction analysis. A new phosphatovanadate crystallized in thortveitite structural type was prepared by the method of hydrothermal synthesis. Anion-forming function of vanadium in the structure formed by cellular layers from Mn-octahedrons joined by ribs and anionic groups PVO7 was determined. It is shown that non-central character of the structure stems from partial ordering of phosphorus and vanadium cations in independent tetrahedral positions. Comparative crystallochemical analysis involving phases of similar composition and structure was made
[ru]
Методом рентгеноструктурного анализа определена кристаллическая структура твердого раствора Mn2(PxV1-x)(VyP1-y)O7: a = 6,794(2), b 8,621(4), c = 4,271(2)A, β = 104,07(3) град., пр.гр. Cm, Z = 2, ρ(выч.) = 3.74 г/см3. Новый фосфатованадат, кристаллизующийся в структурном типе тортвейтита, получен методом гидротермального синтеза. Установлена анионообразующая функция ванадия в структуре, образованной ячеистыми слоями из объединенных ребрами Mn-октаэдров и анионными группами PVO7. Показано, что ацентричный характер структры обусловлен частичным упорядочением катионов фосфора и ванадия в независимых тетраэдрических позициях. Проведен сравнительный кристаллохимический анализ с фазами близкого состава и структурыJournal