[en] High-temperature (1300-1500 grad C) surface nitriding of VT3-1, VT20, 0T4-1 and Vt9 titanium alloys was studied. The alloying metals (Al, Cr, Mo, Si) with lower, in contrast to titanium, affinity to nitrogen were forced back from the surface towards the centre of specimens. In that case, the depth distribution of the alloying metals had a wave-like nature with the obligatory presence at separate sections of the upward diffusion. Behavior mechanism of the alloying metals during nitriding was suggested and a mathematical model to describe that process was introduced
[ru]
Исследовано высокотемпературное (1300-1500 град С) поверхностное азотирование титановых сплавов ВТ3-1, ВТ20, 0Т4-1 и ВТ9. Легирующие металлы (Al, Cr, Mo, Si), имеющие меньшее, чем титан, сродство к азоту, оттесняются от поверхности к центру образцов. При этом распределение легирующих металлов носит волнообразный характер с обязательным присутствием на отдельных участках восходящей диффузии. Предложен механизм поведения легирующих металлов в процессе азотирования и дана математическая модель описания этого процессаJournal