[en] Anionic conductivity of monocrystals of solid solutions Na0.5-xR0.5+xF2+2x (R=Dy, Ho, Tm, Y, combinations Y0.9Nd0.1, Y0.5Yb0.5, Lu0.998Ho0.002, Lu0.9Ho0.1, Lu0.9Nd0.1) with fluorite type structure was studied in a wide range of temperatures (251-1073 K). It was revealed that in the range Tc ≅ 723-773 K change of ion transfer mechanism occurs. At T< Tc the mechanism involves migration of interstitial fluorine ions and mainly depends on defective (cluster) structure of the solid solutions. At T>Tc the mechanism in all probability stems from dissociation of fluorine interstitial ions from the structural clusters. At temperatures above Tc anionic conductivity values reach ∼ 1 S/cm. In crystals Na0.4Ho0.6F2.2 partial decomposition of fluorite solution takes place with formation of compound NaHoF4 featuring gagarinite (NaCaYF6) type structure
[ru]
В широком интервале температур (251-1073 К) исследована анионная проводимость монокристаллов твердых растворов Na0.5-xR0.5+xF2+2x (R=Dy, Ho, Tm, Y, комбинации Y0.9Nd0.1, Y0.5Yb0.5, Lu0.998Ho0.002, Lu0.9Ho0.1, Lu0.9Nd0.1) со структурой типа флюорита. Обнаружено, что в области Тc ≅ 723-773 К происходит смена механизма ионного переноса. При T< Tc механизм связан с миграцией междоузельных ионов фтора и зависит главным образом от дефектной (кластерной) структуры твердых растворов. При Т>Tc механизм, по-видимому, обусловлен диссоциацией междоузельных ионов фтора из структурных кластеров. При температурах выше Тc значения анионной проводимости достигают ∼ 1См/см. В кристаллах Na0.4Ho0.6F2.2 наблюдается частичный распад флюоритового твердого раствора с образованием соединения NaHoF4 с гагаринитовым (NaCaYF6) типом структурыJournal